[1]刘国清,金 懿,吕延文,等.Ce4+掺杂ZnO纳米材料的制备及其光催化性能研究[J].南京师范大学学报(自然科学版),2019,42(02):93-98.[doi:10.3969/j.issn.1001-4616.2019.02.015]
　Liu Guoqing,Jin Yi,Lü Yanwen,et al.Preparation and Photocatalytic Properties ofCe4+-doped ZnO Nano Materials[J].Journal of Nanjing Normal University(Natural Science Edition),2019,42(02):93-98.[doi:10.3969/j.issn.1001-4616.2019.02.015]
点击复制

Ce4+掺杂ZnO纳米材料的制备及其光催化性能研究()
分享到：

《南京师范大学学报》（自然科学版）[ISSN:1001-4616/CN:32-1239/N]

卷:
第42卷
期数:
2019年02期
页码:
93-98
栏目:
·化学·
出版日期:
2019-06-30

文章信息/Info

Title:
Preparation and Photocatalytic Properties ofCe4+-doped ZnO Nano Materials
文章编号:
1001-4616(2019)02-0093-06
作者:
刘国清; 金 懿; 吕延文; 洪辉泉; 李贞攸
衢州学院化学与材料工程学院,浙江 衢州 324000
Author(s):
Liu Guoqing; Jin Yi; Lü Yanwen; Hong Huiquan; Li Zhenyou
College of Chemical and Material Engineering,Quzhou University,Quzhou 324000,China
关键词:
Ce掺杂; ZnO; 光催化; 罗丹明B
Keywords:
Ce-doping; ZnO; photocatalysis; RhB
分类号:
O643
DOI:
10.3969/j.issn.1001-4616.2019.02.015
文献标志码:
A
摘要:
采用水热法通过构建具有MOFs结构的Ce4+掺杂沸石咪唑酯骨架材料ZIF-8前驱体,再高温热解制备了Ce/ZnO光催化纳米材料,利用X射线衍射(XRD)、扫描电镜(SEM)和能谱(EDS)、比表面积测定(BET)对样品结构进行表征. 以罗丹明B(RhB)染料为目标降解物,考察了不同的Ce掺杂量及煅烧温度对Ce/ZnO的结构形貌和光催化性能的影响. 实验结果表明,适量Ce掺杂后,Ce/ZnO粒径均一性与分散性更好,且颗粒更小,比表面积增大,可显著提高其光催化活性和光催化稳定性,煅烧温度过高会出现烧结现象促使光催化性能降低. Ce掺杂量为2%(质量分数),煅烧温度为600 ℃条件下制得的Ce/ZnO光催化性能最佳,对RhB光照降解1 h后降解率超过99%,4次循环催化后降解率仍达97.89%.
Abstract:
Ce/ZnO photocatalytic nanomaterials were prepared by constructing Ce4+-doped zeolite imidazolate skeleton materials ZIF-8 with MOFs structure through hydrothermal method and then high-temperature pyrolysis. The structures of the obtained samples were characterized by X-ray diffraction(XRD),scanning electron microscopy(SEM),energy disperse spectroscopy(EDS)and specific surface area determination(BET). Using RhB dye as the degradation object,the effects of Ce-doping amounts and calcining temperature on the structure morphology and photocatalytic performance of Ce/ZnO was investigated. The experimental results showed that the photocatalytic activity and stability of Ce/ZnO with uniform particle size and better dispersion,smaller particle size and bigger specific surface area,was improved significantly after Ce-doping while too high calcination temperature could cause the photocatalytic performance to be reduced. When the Ce-doping amount is 2%wt and calcination temperature is 600 ℃,the Ce/ZnO with best photocatalytic performance can degrade RhB more than 99% through 1 h lighting and the degradation rate is still up to 97.89% after four cyclic catalysis.

参考文献/References:

[1] KURIAKOSE S,BHARDWAJ N,SINGH J,et al. Structural,optical and photocatalytic properties of flower-like ZnO nanostructures prepared by a facile wet chemical method[J]. J nanotechnol,2013,4:763-770.
[2]余长林,杨凯,余济美. 稀土Ce掺杂对ZnO结构和光催化性能的影响[J]. 物理化学学报,2011,27(2):505-512.
[3]李长全,罗来涛,熊光伟. CeO2/ZnO复合纳米管的制备及其光催化性能的研究[J]. 化学学报,2010,68(10):1023-1026.
[4]REN X L,YING P Z,YANG Z B,et al. Foaming-assisted electrospinning of large-pore mesoporous ZnO nanofibers with tailored structures and enhanced photocatalytic activity[J]. RSC Adv,2015,5(21):16361-16367.
[5]ERIK C,CHIARA G,IIARIA B,et al. Rare earth ions doped ZnO:synthesis,characterization and preliminary photoactivity assessment[J]. Journal of solid state chemistry,2018,264:42-47.
[6]WANG L,JI Z Y,LIN J J,et al. Preparation and optical and photocatalytic properties of Ce-doped ZnO microstructures by simple solution method[J]. Materials science in semiconductor processing,2017,71:401-408.
[7]ANANDAN S,VINU A,Sheeja K L P,et al. Photocatalytic activity of La-doped ZnO for the degradation of monocrotophos in aqueous suspension[J]. J Mol Catal,2007,266(1):149-157.
[8]KHATAMIAN M,KHANDAR A,DIVBAND B,et al. Heterogeneous photocatalytic degradation of 4-Nitrophenol in aqueous suspension by Ln(La3+,Nd3+ or Sm3+)doped ZnO nanoparticles[J]. J Mol Catal,2012,365:120-127.
[9]SUBASH B,KRISHNAKUMAR B,VELMURUGAN R,et al. Synthesis of Ce Co-doped Ag-ZnO photocatalyst with excellent performance for NBB Dye degradation under natural sunlight illumination[J]. Catal Sci Technol,2012,2(11):2319-2326.
[10]XUAN W M,ZHU C F,LIU Y,et al. Mesoporous metal-organic framework materials[J]. Chem Soc Rev,2012,41:1677-1695.
[11]ZHOU H C,LONG J R,YAGHI O M,et al. Introduction to metal-organic frameworks[J]. Chem Rev,2012,112:673-674.
[12]穆翠,枝徐峰,雷威. 功能金属有机骨架材料的应用[J]. 化学进展,2007,9:1345-1356.
[13]张所瀛,刘红,刘朋飞,等. 金属有机骨架材料在CO2/CH4吸附分离中的研究进展[J]. 化工学报,2014(5):1563-1570.
[14]XU L,YIN Z,CAO S,et al. Rational synthesis of triangular Au-Ag2S hybrid nanoframes with effective photoresponses[J]. J chemistry,2014,20(10):2742-2745.
[15]WU Y N,ZHOU M,ZHANG B,et al. Amino acid assisted templating synthesis of hierarchical zeolitic imidazolate framework-8 for efficient arsenate removal[J]. Nanoscale,2014,6(2):1105-1112.
[16]JASON G,JAEYUB C,SANKAR N,et al. Adsorption and diffusion of small alcohols in zeolitic imidazolate frameworks ZIF-8 and ZIF-90[J]. J Phys Chem,2013,117(6):3169-3176.
[17]薛涛,曾舒,毛键,等. 稀土铈掺杂纳米锌的结构及光催化性能研究[J]. 功能材料,2006,37(增):27-30.

备注/Memo

备注/Memo:
收稿日期:2018-09-11.
基金项目:国家自然科学基金(21476128).
通讯联系人:刘国清,工程师,研究方向:纳米半导体光催化材料和“三废”的综合处理研究. E-mail:582873911@qq.com
更新日期/Last Update: 2019-06-30